POLYPROPYLENE P400S

TYPE*

-

-

H*

MELT FLOW RATE

g/10/min

ASTM D 138

3.5

DENSITY

g/cm3

ASTM D 1505

0.910

TENSILE STRENGTH AT YIELD

Kg./cm2

ASTM D 638

380

TENSILE STRENGTH AT BREAK

Kg./cm2

ASTM D 638

350

ELONGATION AT BREAK

%

ASTM D 638

500

IZOD IMPACT STRENGTH AT  23oC

Kg-cm/cm

ASTM D 256

4

IZOD IMPACT STRENGTH AT  0oC

Kg-cm/cm

ASTM D 256

2.5

ROCKWELL HARDNESS

R scale

ASTM D 785

100

FLEXURAL MODULUS

kg./cm2

ASTM D 790

16,000

VICAT SOFTENING POINT

oC

ASTM D 1525

155

HEAT DEFLECTION TEMPERATURE,

 AT 4.6kg/cm2

oC

ASTM D 648

110

AT 18.5kg/cm2

oC

ASTM D 648

60

APPLICATION:

Stretched tape and monofilament for woven bags, woven sheet, ropes, strap and sheet

CHARACTERISTC:

High output, good machanical properties

PROCESSING CONDITION GUIDE:

The quality of products depend on the quality of resins, extruder machines, and extrusion processing condition. Important factors that should be concerned in processing conditions are melt temperature, stretching temperature and stretching ratio. Moreover, line speed in production and finished products make the condition adjustable. Recommended processing condition. Melt temperature - Cast Film 200-260 deg.C, - Blow Film 190 - 220 deg.C, Stretching Temperature 100-140deg.C/ Stretching Ratio 5-7